Microstructures and properties of nickel-titanium carbide composites fabricated by laser cladding

In this work, Ni/TiC composites were synthesized by the laser cladding technique (LCT). A scanning electron microscope (SEM), X-ray diffractometer (XRD), microhardness meter, electrochemical workstation, and friction and wear tester examined the microstructure, surface morphology, phase structure, microhardness, wear, and corrosion resistances of the Ni/TiC composites. These results indicated the Ni/40TiC composite contained finer equiaxed crystals than the Ni and Ni/20TiC composites. In addition, numerous TiC particles in the Ni/40TiC composite impeded growth of the nickel crystals, which resulted in the fine microstructure of the Ni/40TiC composite. The Ni, Ni/20TiC, and Ni/40TiC composites exhibited face-centered cubic (f c c) lattices. The average microhardness values of the Ni/20TiC and Ni/40TiC composites were approximately 748 HV and 851 HV, respectively. The Ni/40TiC composite had the lowest friction coefficient (0.43) among all three coatings, and only some shallow scratches appeared on the surface of the Ni/40TiC composite. The corrosion potential (E) of Ni/40TiC exceeded the Ni/20TiC composite, and both were larger than the Ni composite, which indicated the Ni/40TiC composite had outstanding corrosion resistance and the Ni composite had poor corrosion resistance. The corrosion current densities (i) of Ni, Ni/20TiC, and Ni/40TiC composites were 5.912, 4.405, and 3.248 μA/cm², respectively.     

Cracking behavior and delamination mechanism of lamellar structured TBC with localized mixed oxides

Mixed oxide (MO) with localized growth feature and high growth rate remarkably affects the lifetime of thermal barrier coatings (TBCs), which indicates that clarifying the ceramic cracking mechanism induced by MO is critical for developing new coatings with high durability. Two kinds of TBC models involving spherical and layered mixed oxides are created to explore the influence of MO growth on the local stress state and crack evolution during thermal cycle. The growth of α-Al₂O₃ is also included in the model. The undulating interface between ceramic coat and bond coat is approximated using a cosine curve. Dynamic ceramic cracking is realized by a surface-based cohesive interaction. The ceramic delamination by simulation agrees with the experimental observation. The effects of MO coverage ratio and growth rate on the TBC failure are also discussed. The results show that the MO growth causes the local ceramic coat to bear the normal tensile stress. The failure mode of coating is turned from α-Al₂O₃ thickness control to MO growth control. Once the mixed oxide appears, local ceramic cracking is easy to occur. When multiple cracks connect, ceramic delamination happens. Suppressing MO formation or decreasing MO growth can evidently improve the coating durability. These results in this work can provide important theoretical guidance for the development of anti-cracking TBCs.     

Review on development of metal/ceramic interpenetrating phase composites and critical analysis of their properties

Metal/ceramic composites are in high demand in several industries because of their superior thermo-mechanical properties. Among various composite types, the interpenetrating phase composites (IPCs) with percolating metallic and ceramic phases offer manifold benefits, such as a good combination of strength, toughness, and stiffness, very good thermal properties, excellent wear resistance, as well as the flexibility of microstructure and processing route selection, etc. The fabrication of metal/ceramic IPCs typically involves two steps - i) processing of an open porous ceramic body, and ii) infiltration of metallic melt in the pores to fabricate the IPC. Although significant progress has been made in recent years for developing both porous ceramics and melt infiltration methods, to the best of the knowledge of the authors, no review article summarizing all the aspects of processing and properties of IPCs has been published till date. This review article is aimed at filling this gap. Starting with a brief introduction about the current status and applications of IPCs, the various processing routes for fabricating open porous ceramic preforms and melt infiltration techniques have been discussed. Subsequently, the data available for various important physical, mechanical, and thermal properties for IPCs have been critically analyzed to thoroughly understand their dependence on various structural and processing parameters. To compare the properties of IPCs with other relevant materials, seven different Ashby material property maps have been used, and the domains for IPCs have been created in them. For each map, the concept of material indices has been employed to critically discuss how IPCs perform in relation to other material classes for various optimum design conditions. Finally, a detailed future outlook for further research on IPCs has been provided.     

Cryptographic Lightweight Encryption Algorithm with Dimensionality Reduction in Edge Computing

Edge Computing is one of the radically evolving systems through generations as it is able to effectively meet the data saving standards of consumers, providers and the workers. Requisition for Edge Computing based items have been increasing tremendously. Apart from the advantages it holds, there remain lots of objections and restrictions, which hinders it from accomplishing the need of consumers all around the world. Some of the limitations are constraints on computing and hardware, functions and accessibility, remote administration and connectivity. There is also a backlog in security due to its inability to create a trust between devices involved in encryption and decryption. This is because security of data greatly depends upon faster encryption and decryption in order to transfer it. In addition, its devices are considerably exposed to side channel attacks, including Power Analysis attacks that are capable of overturning the process. Constrained space and the ability of it is one of the most challenging tasks. To prevail over from this issue we are proposing a Cryptographic Lightweight Encryption Algorithm with Dimensionality Reduction in Edge Computing. The t-Distributed Stochastic Neighbor Embedding is one of the efficient dimensionality reduction technique that greatly decreases the size of the non-linear data. The three dimensional image data obtained from the system, which are connected with it, are dimensionally reduced, and then lightweight encryption algorithm is employed. Hence, the security backlog can be solved effectively using this method.     

Growth mechanism and gas-sensing characteristics of organic-additive-free zinc oxide of various shapes

Zinc oxide is widely used in gas sensors, solar cells, and photocatalysts because of its wide bandgap and exciton binding energy of 60 meV in various metal oxides. To use ZnO as a gas sensor, it is necessary to synthesize it with surface defects and a large specific surface area. In this study, hydrothermal synthesis without surfactants was employed to obtain organic-additive-free ZnO. For morphology control, we varied the ratio of the hydroxide ion concentration to the zinc ion concentration. To confirm the growth mechanism of ZnO, we performed X-ray diffraction, scanning electron microscopy, and transmission electron microscopy analyses. Raman spectroscopy and photoluminescence measurements were performed to analyze the surface properties. The Brunauer–Emmett–Teller method and probe stations were used to measure the specific surface area and sensitivity of the gas sensor, respectively. The results confirmed that flower-shaped ZnO is the most suitable gas-sensing material.     

Simulation of thermal barrier coating spallation induced by the initiation/growth/coalescence of internal crack and interfacial crack based on a real image model

In the furnace cycle test, the growth of oxide film leads to the propagation and coalescence of multiple cracks near the interface, which should be responsible for the spallation of thermal barrier coatings (TBCs). A TBC model with real interface morphology is created, and the near-interface large pore is retained. The purpose of this work is to clarify the mechanism of TBC spallation caused by successive initiation, propagation, and linkage of cracks near the interface during thermal cycle. The dynamic growth of thermally grown oxide (TGO) is carried out by applying a stress-free strain. The crack nucleation and arbitrary path propagation in YSZ and TGO are simulated by the extended finite element method (XFEM). The debonding along the YSZ/TGO/BC interface is evaluated using a surface-based cohesive behavior. The large-scale pore in YSZ near the interface can initiate a new crack. The ceramic crack can propagate to the YSZ/TGO interface, which will accelerate the interfacial damage and debonding. For the TGO/BC interface, the normal compressive stress and small shear stress at the valley hinder the further crack propagation. The growth of YSZ crack and the formation of through-TGO crack are the main causes of TBC delamination. The accelerated BC oxidation increases the lateral growth strain of TGO, which will promote crack propagation and coalescence. The optimization design proposed in this work can provide another option for developing TBC with high durability.     

Community involvement critical for revitalization: Grass-roots initiative key to environmental remediation and restoration in the Great River (St. Lawrence River)

This paper describes the creation of an environmentally conscious community group, the Great River Network, and the role that it has played in the remediation and restoration process as part of one of the Great Lakes environmental programs. Community engagement was initiated in the region as part of the Remedial Action Plan for the Area of Concern at Cornwall/Akwesasne/Massena within the Upper St. Lawrence River. The community group formalised as a network representing 50+ organisations in response to perceived inadequacies in the agency of the community to respond to new environmental concerns outside of the scope of the existing programs. As a grass-roots initiative, the Great River Network has successfully completed remediation and restoration actions of significant value to the environment. These include a series of river clean ups (>42 tonnes of garbage removed), fish habitat restoration, and addressing shoreline erosion issues. Success has been achieved through partnering with a range of organisations, including Indigenous, non-profit, governmental, Conservation Authorities, businesses and industry partners. The action-oriented approach showcases how remediation and restoration led by, and embedded in, the community can result in true revitalization. A simplified framework for adaptive management practices for remediation and restoration efforts that lead to revitalization, including knowledge translation, is proposed. This case study highlights the transformational opportunities that remediation and restoration initiatives can bring. In this instance, the process is intensely local and cooperative and lays the foundation for moving towards a collective impact approach for the region.     

Joining zirconia with nickel-based superalloys for extreme applications by using a pressure-free high-temperature resistant adhesive

In order to meet the high demand for joining ceramic/superalloy composite structure in extreme environments, a novel high-temperature resistant adhesion technique was developed for joining ZrO₂ and Inconel 625 by applying an aluminum phosphate emulsion/zirconium sol based adhesive. With increasing temperature, a series of reactions occurred in adhesive, and its high-temperature bonding was attributed to the formation of a composite structure containing various ceramics and intermetallics. The adhesive after RT curing could find direct applications in extreme environments, and provide bonding strength no less than 2.5 MPa in the temperature range of RT-1100 °C. The bonding strength was higher than 4 MPa in the temperature range of 800–1000 °C, which was further attributed to the formation of an effective CTE-gradient relationship among ZrO₂, adhesive and Inconel 625, as well as the interfacial reactions between the two substrates. The work broadened the application of adhesion technique and brought new ideas for joining dissimilar engineering materials.     

Preparation and pore-forming mechanism of MgO–Al2O3–CaO-based porous ceramics using phosphorus tailings

A simple strategy for preparing MgO–Al₂O₃–CaO-based porous ceramics (MACPC) with high strength and ultralow thermal conductivity has been proposed in this work based on the raw material of phosphorus tailings. The effects of phosphorus tailings content, carbon black addition and heat treatment temperature on the properties of MACPC were studied, and their pore-forming mechanism during sintering was revealed. The results showed that the main phase composition of MACPC was magnesia alumina spinel and calcium aluminate after sintering at 1225 °C. Furthermore, the MACPC exhibited excellent comprehensive properties when 60 wt% phosphorus tailings and 40 wt% alumina were added, whose apparent porosity was 62.8%, cold compressive strength was 14.8 MPa, and the thermal conductivity was 0.106 W/(m·K) at 800 °C. The synchronously enhanced strength and thermal insulation properties of MACPC were related to the formation of uniformly distributed micropores (<2 μm) and passages in the matrix, which originated from the decomposition of phosphorus tailings and the burnt out of carbon black during the sintering process. The preparation of MACPC with high temperature resistance and excellent mechanical and thermal insulation properties with the raw material of phosphorus tailings provided an effective method for the high-value utilization of phosphorus tailings.     

Orthorhombic to tetragonal polymorphic transformation of YTa3O9 and its inhibition through the design of high-entropy (Y0.2La0.2Ce0.2Nd0.2Gd0.2)Ta3O9

To explore the mechanism of phase transformation, YTa₃O₉ was prepared by an integrated one-step synthesis and sintering method at 1500 °C using Y₂O₃ and Ta₂O₅ powders as starting materials. High-temperature XRD patterns and Raman spectra showed that a phase transformation from orthorhombic to tetragonal took place in YTa₃O₉ through the bond length and angle changes at 300–400 °C, which caused a thermal conductivity rise. To inhibit the phase transformation, a high-entropy (Y_0.2La_0.2Ce_0.2Nd_0.2Gd_0.2)Ta₃O₉ (HE RETa₃O₉) was designed and synthesized at 1550 °C using the integrated solid-state synthesis and sintering method. In tetragonal structured HE RETa₃O₉, phase transformation was inhibited by the high-entropy effect. Furthermore, HE RETa₃O₉ exhibited low thermal conductivity, and its tendency to increase with temperature was alleviated (1.69 W/m·K, 1073 K). Good phase stability, low thermal conductivity and comparable fracture toughness to YSZ make HE RETa₃O₉ promising as a new thermal barrier coating material.